Neodymium-doped yttrium orthovanadate

Neodymium-doped yttrium orthovanadate (Nd:YVO₄) is a crystalline material formed by adding neodymium ions to yttrium orthovanadate. It is commonly used as an active laser medium for diode-pumped solid-state lasers. It comes as a transparent blue-tinted material. It is birefringent, therefore rods made of it are usually rectangular.

As in all neodymium-doped laser crystals, the lasing action of Nd:YVO₄ is due to its content of neodymium ions, which may be excited by visible or infrared light, and undergo an electronic transition resulting in emission of coherent infrared light at a lower frequency, usually at 1064 nm (other transitions in Nd are available, and can be selected for by external optics).

Basic properties

• Atomic density: ~1.37×10²⁰ atoms/cm³
• Crystal structure:
  • zircon tetragonal (tetragonal bipyramidal)
  • space group D_4h
  • a=b=7.12, c=6.29
• Density: 4.22 g/cm³
• Mohs hardness: Glass-like, ~5
• Thermal expansion coefficient:
  • α_a=4.43×10⁻⁶/K
  • α_c=11.37×10⁻⁶/K
• Thermal conductivity:
  • parallel to C-axis: 5.23 W·m⁻¹·K⁻¹
  • perpendicular to C-axis: 5.10 W·m⁻¹·K⁻¹

Optical properties

• Lasing wavelengths : 914 nm, 1064 nm, 1342 nm
• Crystal class : positive uniaxial, n_o=n_a=n_b, n_e=n_c,
  • n_o=1.9573, n_e=2.1652, at 1064 nm
  • n_o=1.9721, n_e=2.1858, at 808 nm
  • n_o=2.0210, n_e=2.2560, at 532 nm
• Fluorescence lifetime (spontaneous emission lifetime) as a function of Nd ions concentration:

• Absorption cross-section at 808 nm : 5.5×10⁻²⁰ cm²
• Emission cross-section at 1064 nm : 38×10⁻¹⁹ cm² (Reference: JOSA 66, 1405-1414 (1976).)
• Polarized laser emission : π-polarization; parallel to optic axis (c-axis) (for a-cut crystal)
• Gain bandwidth : 0.96 nm (257 GHz) at 1064 nm (for 1.1 atm% Nd doped)
• Absorption coefficients at 808 nm for different doping conenctrations:

See also

• Yttrium aluminium garnet (YAG)

References

• H. E. Rast; H. H. Caspers & S. A. Miller (1968). "Infrared Spectral Emittance and Optical Properties of Yttrium Vanadate" (abstract). Phys. Rev. 169 (3): 705–709. Bibcode:1968PhRv..169..705R. doi:10.1103/PhysRev.169.705. 
• O. Guillot-Noel; B. Bellamy; B. Viana; D. Gourier (1999). "Correlation between rare-earth oscillator strengths and rare-earth–valence-band interactions in neodymium-doped YMO4 (M=V, P, As), Y3Al5O12, and LiYF4 matrices" (abstract). Phys. Rev. B. 60 (3): 1668–1677. Bibcode:1999PhRvB..60.1668G. doi:10.1103/PhysRevB.60.1668.